35 OZ Grey High Temperature Fiberglass Cloth Calcium Silicate Coating
Description:
TGF1200S-CS213-5030 is a stainless steel wire inserted woven texturized fiberglass fabric coated with a formulated inorganic solution which provides high temperature and abrasion resistance properties for the manufacturer of gaskets, flexible expansion joints, removable jackets and other types of fire control systems.
TGF1200S-CS213-5030 withstands temperature extremes of up to 750 0C, no significant deterioration in flexibility or strength, without smoke/fumes release when catches fire.
Date sheet:
| BASE FABRIC | Base fabric style No. TGF1200S | |||
| (Metric) | (English) | Test methods | ||
| Weave | Panama | Panama | ||
| Yarn | ||||
| Warp | ET9 1250 tex S.S 316# wire | ETG 4.0 S.S 316# wire | ||
| Weft | ET9 770 tex S.S 316# wire | ETG 6.5 S.S 316# wire | ||
| Construction | ||||
| Warp | 6 ± 0.6 ends /cm | 15 ± 2 ends/inch | ASTM D 3775-96 | |
| Weft | 5.5 ± 0.5 picks /cm | 14 ± 2 picks/inch | ASTM D 3775-96 | |
| Weight | 1200 ± 50 g/m2 | 35 ± 1.47 oz/yd2 | ASTM D3776-96 | |
| Thickness | 1.4 ± 0.07 mm | 0.055 ± 0.003 inch | ASTM D1777-96 | |
| COATED FABRIC | Coating style No. CS213-5030 | |||
| Coating | Formulated inorganic solutions coated on both sides | |||
| Weight | 1220 ± 50 g/m2 | 36 ± 1.47 oz/yd2 | ASTM D3776-96 | |
| Thickness | 1.4 ± 0.07 mm | 0.055 ± 0.003 inch | ASTM D1777-96 | |
| Color | Grey | |||
| Temp resistance | 7500C for the coating 8000C for the base fabric | |||
Application:
High temperature welding blanket
Removable insulation mattress, jacket & pad
Fire doors/smoke curtain
Dusts filter bag
Flexible expansion joints & compensators
Advantages:
Excellent anti abrasion property
Easy to be cut, sewn and fabricated