High Temperature Fabric Heat Resistant Fiberglass Cloth Manufacturer.
Add to Cart
Acrylic Coated Fiberglass Fabrics Heat Resistant Cloth For Fireproof & Welding Protection & Hullboard
Weave-lock finished fiberglass fabrics
The weave-lock treatment stiffens the fabric slightly to reduce the amount of fraying during fabrication. The weave-lock finished fiberglass fabric enables the user to cut, sew and punch holes more effectively.
Main applications:
-Shipbuilding
-Welding blankets, fire blankets
-Fire doors, fire curtains, smoke curtains
-Other fire control systems
| BASE FABRIC | Base fabric style No. TGF880 | |||
| (Metric) | (English) | Test methods | ||
| Weave | 4 harness satin | Crowfoot | ||
| Yarn | ||||
| Warp | ET9 480 tex | ETG 8.6 | ||
| Weft | ET9 480 tex | ETG 8.6 | ||
| Construction | ||||
| Warp | 10 ± 0.6 ends/cm | 25 ± 2 ends/inch | ASTM D 3775-96 | |
| Weft | 8 ± 0.5 picks/cm | 20 ± 1 picks/inch | ASTM D 3775-96 | |
| Weight | 880 ± 40 g/m2 | 25.8 ± 1.2 oz/yd2 | ASTM D3776-96 | |
| Thickness | 1.0 ± 0.1 mm | 0.039 ± 0.005 inch | ASTM D1777-96 | |
| COATED FABRIC | Coating style No. AC225-3008 | |||
| Coating | Acrylic weave-set finish on both sides, high add-on. | |||
| Weight | 910 ± 40 g/m2 | 27 ± 1.2 oz/yd2 | ASTM D3776-96 | |
| Thickness | 1.05 ± 0.1 mm | 0.043 ±0.005 inch | ASTM D1777-96 | |
| Color | Black | |||
| Temp resistance | 5500C | 10000F | ||